YUCERA 1200MPA 98mm 95mm Beyaz Çok Katmanlı Zirkonya Disk
YUCERA Dedntal Materials Manufacturer Dental Laboratory Economical Zirconia Block Multilayer Zirconia Disc Features 1, Zirconium dioxide porcelain tooth is a mineral that exists in nature as oblique zircon. Its density and strength are very high, the strength is 1.5 times higher than that of EMPRESS II, more than 60% higher than INCERAM zirconia, combined with unique crack resistance and strong curing performance after cracking, it can make porcelain bridges of more than 6
-
Beyaz 98mm 95mm Cam Cad 1530 ℃ Dental Zirkonya Bloğu
Labs Conusmable Cad Cam Matrials Dental Zirconia Blocks YUCERA High Translucent High Translucency Zirconia Perfect For Anterior Restorarion , Dental Zirconia Blank YUCERA blanks are made from biocompatible zirconiumdioxyde. The yttrium oxide stabilizing protects the material against cracks and increases the tensile and compressive strength. The special grain size allocation inside the material and the added aluminium oxide also result in extra strength during milling and
-
1200MPA Cad Cam Blokları 98mm Beyaz Diş Zirkonya Bloğu
Dental+Consumables YUCERA HT Dental Zirconia Cad Cam Materials Manufacturer Product Features Safety:No irritation,No corrosion,Good bio-compatibility Beauty:Natural teeth color can be reproduced Comfortability:Low thermal conductivity,hot and cold changes do not stimulte the pulp Durability:Over 1600MPa perturbed strength, durable and useful Zirconia Dental Material Blank Superior Strength High Translucency Zirconia YUCERA HT high strength and high translucency, one of the
-
Odontologia Aletli HT 1200MPA Dental Zirkonya Diskleri
Odontologia Instrumental Zirconia Dental Materiall Yucera HT Economical Zirconia Block Feature high flexural strength, fracture resistance, exceptional durability, and easy milling properties with precision. Polish or Glaze after Sintering Ideal for full contour crowns and bridges Benefits Reduce preparation dramatically No need for porcelain Restoration seated firmly Eliminates the possibility of porcelain chipping No need to take out restoration under imaging medical
-
Cad Cam Freze Makinesi için 98mm Beyaz Pediatrik Zirkonya Kronları
Dental Zirconia Pediatric Zirconia Crowns For Dental Lab Cad Cam Milling Machine HT/ST Sintering Curve (1-5) HT/ST Sintering Curve (1-5) Sintering step Start Temperature(℃) End Temperature(℃) Time(Min) Rate(℃/Min) Step 1 20 300 30 9.3 Step 2 300 1200 150 6 Step 3 1200 1530 110 3 Step 4 1530 1530 120 0 Step 5 1530 800 100 -7.3 Step 6 800 natural cooling 20 120 -6.5 HT/ST Sintering Curve (10 units) Sintering step Start Temperature(℃) End Temperature(℃) Time(Min) Rate(℃/Min)
-
Dental Malzemeler YUCERA HT Beyaz Çok Katmanlı Zirkonya Blok
Other Dental Equipments YUCERA Dental Direkt Zirconia Blocks For Dental Lab Zirconia Block Introduction YUCERA zirconia block has high strength, excellent permeability and color aesthetic repair effect that suitable for CAD/CAM system and manual system. Product Features Safety:No irritation,No corrosion,Good bio-compatibility Beauty:Natural teeth color can be reproduced Comfortability:Low thermal conductivity,hot and cold changes do not stimulte the pulp Durability:Over
-
98x10mm 1530 ℃ Laboratuvar Ekipmanları İçin Diş Zirkonya Bloğu
YUCERA Dental Manufacturer Dental Zirconia Blocks For Laboratory Equipment Zirconia Features Zirconium dioxide porcelain tooth is a mineral that exists in nature as oblique zircon. Its density and strength are very high, the strength is 1.5 times higher than that of EMPRESS II, more than 60% higher than INCERAM zirconia, combined with unique crack resistance and strong curing performance after cracking, it can make porcelain bridges of more than 6 units. The problem that all
-
Laboratuvar için 98x10mm Beyaz 1200MPA Diş Zirkonya Boş
YUCERA Dental Materials And Equipment Manufacturer Economical Dental Zirconia Blanks For Dental Laboratory To achieve expected quality, the sintering curves must be followed. Note: please employ high-temperature furnace specially designed for denture manufacturing. It is good for ceramics sintering to prolong heating up time and cooling time properly. 1. Sintering preparation: Make sure there is enough sintering space to avoid deformation. After dyeing, the restoration must